phi0 = 0.87 Quenches

We present the results of the systems with an initial LC composition (area fraction) of 0.87 .

F1-2 Run: phi0=0.87 T=0.75 N=150

Initially unstable with respect to PS and PO, but more unstable with respect to PO.

PS significant by t=1.4. PO significant by t=1.4. See separate analysis on this quench.

Resulting intermediate/late-time structure: Noncircular polymer-rich domains (minor phase) in a LC-rich matrix (major phase). View phi and S profiles.

#5: new" k₁ -- from phi-based S(k).

G61-2 Run: phi0=0.87 T=0.85 N=150

Initially unstable with respect to PS only.

PS significant by t=. PO significant by t=. See separate analysis on this quench.

Resulting intermediate/late-time structure: Noncircular polymer-rich domains (minor phase) in a LC-rich matrix (major phase). View phi and S profiles.

#6: new" k₁ -- from phi-based S(k).

Jump to the individual results of the quench with (phi0, T, N) of:

A2: 0.76, 0.95, 100	A21-2: 0.76, 0.95, 150	A4: 0.68, 0.95, 100	A4-1: 0.68, 0.95, 150	A41-250-2: 0.68, 0.95, 250
F31-2: 0.68, 0.75, 150	H21-2: 0.75, 0.75, 150	H41-2: 0.80, 0.75, 150	F61-2: 0.83, 0.75, 150	F21-2: 0.84, 0.75, 150
C2-1: 0.85, 0.75, 150	C21-250-2: 0.85, 0.75, 250	F5-2: 0.86, 0.75, 150	F11-2: 0.87, 0.75, 150	F4a-2: 0.88, 0.75, 150
E7-2: 0.89, 0.75, 150	E71-250-2: 0.89, 0.75, 250	G11-2: 0.68, 0.85, 150	H11-2: 0.75, 0.85, 150	H31-2: 0.80, 0.85, 150
G21-2: 0.83, 0.85, 150	G31-2: 0.84, 0.85, 150	G41-2: 0.85, 0.85, 150	G51-2: 0.86, 0.85, 150	G61-2: 0.87, 0.85, 150

Other links:

• Additional Quenches -- an overview
  • T=0.75 Quenches
  • T=0.85 Quenches
  • phi0=0.68 Quenches
  • phi0=0.83 Quenches
  • phi0=0.84 Quenches
  • phi0=0.85 Quenches
  • phi0=0.86 Quenches
  • phi0=0.87 Quenches
• Critical Quench Comparison
• Off-critical Quench Comparison

Last updated August 1, 1999.